[FLUOROSINT®]
|
Fluorosint® 500
| Properties |
Test Methods |
Units |
Values |
| Density |
ASTM D-792 |
– |
2.32 |
| Tensile Strength at 23°C |
ASTM D-638 |
MPa |
9.3 |
| {kgf/cm2} |
{95} |
Tensile Elongation at 23°C
(at break) |
ASTM D-638 |
% |
10 |
| Tensile Modulus at 23°C |
ASTM D-638 |
MPa |
– |
| {103kgf/cm2} |
– |
Compressive Strength at 23°C
(5% Deformation) |
ASTM D-695 |
MPa |
28 |
| {kgf/cm2} |
{290} |
| Compressive Modulus at 23°C |
ASTM D-695 |
MPa |
2,520 |
| {103kgf/cm2} |
{23} |
| Flexural Strength at 23°C |
ASTM D-790 |
MPa |
18 |
| {kgf/cm2} |
{190} |
| Flexural Modulus at 23°C |
ASTM D-790 |
MPa |
3,330 |
| {103kgf/cm2} |
{34} |
| Izod Impact (Notched) |
ASTM D-256 |
J/m |
54 |
| {kgf·cm/2.54cm} |
{14} |
| Rockwell Hardness at 23°C |
ASTM D-785 |
R scale |
65 |
| Heat Deflection Temperature |
ASTM D-648 |
°C |
132 |
| 1.820MPa |
| {18.6kgf/cm2} |
| 0.445MPa |
ASTM D-648 |
°C |
– |
| {4.6kgf/cm2} |
| Coefficient of Liner Thermal Expansion |
ASTM D-696 |
×10-5/°C |
3.4 |
| Continuous Service Temperature |
– |
°C |
260 |
| Water Absorption Immersion at 23°C |
ASTM D-570 |
% |
|
| (24h in water) |
0.1 |
| (Saturation) |
3.0 |
| Volume Resistivity at 23°C |
ASTM D-257 |
Ω·m |
>1011 |
| {Ω·cm} |
{>1013} |
| Dielectric Strength |
ASTM D-149 |
kV/mm |
10.8 |
| Flammability |
UL94 |
– |
(V-0) |
| * |
The data in the table shows the representive data, though they are not the guaranteed ones. |
Fluorosint® 207
| Properties |
Test Methods |
Units |
Values |
| Density |
ASTM D-792 |
– |
2.30 |
| Tensile Strength at 23°C |
ASTM D-638 |
MPa |
11 |
| {kgf/cm2} |
{120} |
Tensile Elongation at 23°C
(at break) |
ASTM D-638 |
% |
75 |
| Tensile Modulus at 23°C |
ASTM D-638 |
MPa |
– |
| {103kgf/cm2} |
– |
Compressive Strength at 23°C
(5% Deformation) |
ASTM D-695 |
MPa |
19 |
| {kgf/cm2} |
{200} |
| Compressive Modulus at 23°C |
ASTM D-695 |
MPa |
1,470 |
| {103kgf/cm2} |
{15} |
| Flexural Strength at 23°C |
ASTM D-790 |
MPa |
20 |
| {kgf/cm2} |
{210} |
| Flexural Modulus at 23°C |
ASTM D-790 |
MPa |
1,960 |
| {103kgf/cm2} |
{20} |
| Izod Impact (Notched) |
ASTM D-256 |
J/m |
96 |
| {kgf·cm/2.54cm} |
{25} |
| Rockwell Hardness at 23°C |
ASTM D-785 |
R scale |
60 |
| Heat Deflection Temperature |
ASTM D-648 |
°C |
98 |
| 1.820MPa |
| {18.6kgf/cm2} |
| 0.445MPa |
ASTM D-648 |
°C |
– |
| {4.6kgf/cm2} |
| Coefficient of Liner Thermal Expansion |
ASTM D-696 |
×10-5/°C |
10.3 |
| Continuous Service Temperature |
– |
°C |
260 |
| Water Absorption Immersion at 23°C |
ASTM D-570 |
% |
|
| (24h in water) |
0.03 |
| (Saturation) |
– |
| Volume Resistivity at 23°C |
ASTM D-257 |
Ω·m |
>1010 |
| {Ω·cm} |
{>1012} |
| Dielectric Strength |
ASTM D-149 |
kV/mm |
7.8 |
| Flammability |
UL94 |
– |
(V-0) |
| * |
The data in the table shows the representive data, though they are not the guaranteed ones. |
|