| Properties |
Test Methods |
Units |
Values |
| Density |
ASTM D-792 |
– |
1.15 |
| Tensile Strength at 23°C |
ASTM D-638 |
MPa |
88 |
| {kgf/cm2} |
{900} |
Tensile Elongation at 23°C
(at break) |
ASTM D-638 |
% |
50 |
| Tensile Modulus at 23°C |
ASTM D-638 |
MPa |
3,236 |
| {103kgf/cm2} |
{33} |
Compressive Strength at 23°C
(Yield) |
ASTM D-695 |
MPa |
98 |
| {kgf/cm2} |
{1,000} |
| Compressive Modulus at 23°C |
ASTM D-695 |
MPa |
– |
| {103kgf/cm2} |
– |
| Flexural Strength at 23°C |
ASTM D-790 |
MPa |
103 |
| {kgf/cm2} |
{1,050} |
| Flexural Modulus at 23°C |
ASTM D-790 |
MPa |
– |
| {103kgf/cm2} |
– |
| Izod Impact (Notched) |
ASTM D-256 |
J/m |
97 |
| {kgf·cm/2.54cm} |
{25} |
| Rockwell Hardness at 23°C |
ASTM D-785 |
R scale |
115 |
| Heat Deflection Temperature |
ASTM D-648 |
°C |
110 |
| 1.820MPa |
| {18.6kgf/cm2} |
| 0.445MPa |
ASTM D-648 |
°C |
170 |
| {4.6kgf/cm2} |
| Coefficient of Liner Thermal Expansion |
ASTM D-696 |
×10-5/°C |
9.0 |
| Continuous Service Temperature |
– |
°C |
110 |
| Water Absorption Immersion at 23°C |
ASTM D-570 |
% |
|
| (24h in water) |
1.2 |
| (Saturation) |
8.5 |
| Volume Resistivity at 23°C |
ASTM D-257 |
Ω·m |
6×1012 |
| {Ω·cm} |
{6×1014} |
| Dielectric Strength |
ASTM D-149 |
kV/mm |
19 |
| Flammability |
UL94 |
– |
(HB) |
| * |
The data in the table shows the representive data, though they are not the guaranteed ones. |
| * |
Combustion property is presented according to UL standard evaluation test and data presented by raw material producers. No products need caution as a material. |
|