MC NYLON

Polyamides 6 (PA6)

 Property
Stock Shapes

>Property Back to Details

MC901

MC900NC

MC801

MC928-IR

MC703HL

MC602ST

MC501CD R2

MC501CD R6

MC501CD R9

MC500AS R11

MC901

Properties Test Methods Units Values
Density ASTM D-792
–
 1.16
Tensile Strength at 23°C ASTM D-638 MPa 96
{kgf/cm2} {980}
Tensile Elongation at 23°C
(at break)		 ASTM D-638 % 30
Tensile Modulus at 23°C ASTM D-638 MPa 3,432
{103kgf/cm2} {35}
Compressive Strength at 23°C
(5% Deformation)		 ASTM D-695 MPa 95
{kgf/cm2} {970}
Compressive Modulus at 23°C ASTM D-695 MPa 3,530
{103kgf/cm2} {36}
Flexural Strength at 23°C ASTM D-790 MPa 110
{kgf/cm2} {1,120}
Flexural Modulus at 23°C ASTM D-790 MPa 3,530
{103kgf/cm2} {36}
Izod Impact (Notched) ASTM D-256 J/m 50
{kgf·cm/2.54cm} {13}
Rockwell Hardness at 23°C ASTM D-785 R scale 120
Heat Deflection Temperature ASTM D-648 °C 200
1.820MPa
{18.6kgf/cm2}
0.445MPa ASTM D-648 °C 215
{4.6kgf/cm2}
Coefficient of Liner Thermal Expansion ASTM D-696 ×10-5/°C 9.0
Continuous Service Temperature
–
 °C 120
Water Absorption Immersion at 23°C ASTM D-570 %  
(24h in water) 0.8
(Saturation) 6.0
Volume Resistivity at 23°C ASTM D-257 Ω·m 4.2×1013
{Ω·cm} {4.2×1015}
Dielectric Strength ASTM D-149 kV/mm 20
Flammability UL94
–
 (HB)
* The data in the table shows the representive data, though they are not the guaranteed ones.
* Combustion property is presented according to UL standard evaluation test and data presented by raw material producers. No products need caution as a material.
TOP

MC900NC

Properties Test Methods Units Values
Density ASTM D-792
–
 1.16
Tensile Strength at 23°C ASTM D-638 MPa 96
{kgf/cm2} {980}
Tensile Elongation at 23°C
(at break)		 ASTM D-638 % 30
Tensile Modulus at 23°C ASTM D-638 MPa 3,432
{103kgf/cm2} {35}
Compressive Strength at 23°C
(5% Deformation)		 ASTM D-695 MPa 95
{kgf/cm2} {970}
Compressive Modulus at 23°C ASTM D-695 MPa 3,530
{103kgf/cm2} {36}
Flexural Strength at 23°C ASTM D-790 MPa 110
{kgf/cm2} {1,120}
Flexural Modulus at 23°C ASTM D-790 MPa 3,530
{103kgf/cm2} {36}
Izod Impact (Notched) ASTM D-256 J/m 50
{kgf·cm/2.54cm} {13}
Rockwell Hardness at 23°C ASTM D-785 R scale 120
Heat Deflection Temperature ASTM D-648 °C 200
1.820MPa
{18.6kgf/cm2}
0.445MPa ASTM D-648 °C 215
{4.6kgf/cm2}
Coefficient of Liner Thermal Expansion ASTM D-696 ×10-5/°C 9.0
Continuous Service Temperature
–
 °C 120
Water Absorption Immersion at 23°C ASTM D-570 %  
(24h in water) 0.8
(Saturation) 6.0
Volume Resistivity at 23°C ASTM D-257 Ω·m 4.2×1013
{Ω·cm} {4.2×1015}
Dielectric Strength ASTM D-149 kV/mm 20
Flammability UL94
–
 (HB)
* The data in the table shows the representive data, though they are not the guaranteed ones.
* Combustion property is presented according to UL standard evaluation test and data presented by raw material producers. No products need caution as a material.
TOP

MC801

Properties Test Methods Units Values
Density ASTM D-792
–
 1.16
Tensile Strength at 23°C ASTM D-638 MPa 83
{kgf/cm2} {850}
Tensile Elongation at 23°C
(at break)		 ASTM D-638 % 40
Tensile Modulus at 23°C ASTM D-638 MPa 3,334
{103kgf/cm2} {34}
Compressive Strength at 23°C
(5% Deformation)		 ASTM D-695 MPa 93
{kgf/cm2} {948}
Compressive Modulus at 23°C ASTM D-695 MPa 3,513
{103kgf/cm2} {35.8}
Flexural Strength at 23°C ASTM D-790 MPa 110
{kgf/cm2} {1,120}
Flexural Modulus at 23°C ASTM D-790 MPa
–
{103kgf/cm2}
–
Izod Impact (Notched) ASTM D-256 J/m 50
{kgf·cm/2.54cm} {13}
Rockwell Hardness at 23°C ASTM D-785 R scale 120
Heat Deflection Temperature ASTM D-648 °C 200
1.820MPa
{18.6kgf/cm2}
0.445MPa ASTM D-648 °C 215
{4.6kgf/cm2}
Coefficient of Liner Thermal Expansion ASTM D-696 ×10-5/°C 9.0
Continuous Service Temperature
–
 °C 120
Water Absorption Immersion at 23°C ASTM D-570 %  
(24h in water) 0.8
(Saturation) 6.0
Volume Resistivity at 23°C ASTM D-257 Ω·m
–
{Ω·cm}
–
Dielectric Strength ASTM D-149 kV/mm 18
Flammability UL94
–
 (HB)
* The data in the table shows the representive data, though they are not the guaranteed ones.
* Combustion property is presented according to UL standard evaluation test and data presented by raw material producers. No products need caution as a material.
TOP

MC928-IR

Properties Test Methods Units Values
Density ASTM D-792
–
 1.15
Tensile Strength at 23°C ASTM D-638 MPa 66
{kgf/cm2} {673}
Tensile Elongation at 23°C
(at break)		 ASTM D-638 % 46
Tensile Modulus at 23°C ASTM D-638 MPa
–
{103kgf/cm2}
–
Compressive Strength at 23°C
(5% Deformation)		 ASTM D-695 MPa 77
{kgf/cm2} {785}
Compressive Modulus at 23°C ASTM D-695 MPa 3,267
{103kgf/cm2} {33.3}
Flexural Strength at 23°C ASTM D-790 MPa 100
{kgf/cm2} {1,020}
Flexural Modulus at 23°C ASTM D-790 MPa 2,984
{103kgf/cm2} {30.4}
Izod Impact (Notched) ASTM D-256 J/m 71
{kgf·cm/2.54cm} {18}
Rockwell Hardness at 23°C ASTM D-785 R scale 115
Heat Deflection Temperature ASTM D-648 °C 195
1.820MPa
{18.6kgf/cm2}
0.445MPa ASTM D-648 °C 210
{4.6kgf/cm2}
Coefficient of Liner Thermal Expansion ASTM D-696 ×10-5/°C 9.5
Continuous Service Temperature
–
 °C 110
Water Absorption Immersion at 23°C ASTM D-570 %  
(24h in water)
–
(Saturation)
–
Volume Resistivity at 23°C ASTM D-257 Ω·m
–
{Ω·cm}
–
Dielectric Strength ASTM D-149 kV/mm
–
Flammability UL94
–
 (HB)
* The data in the table shows the representive data, though they are not the guaranteed ones.
* Combustion property is presented according to UL standard evaluation test and data presented by raw material producers. No products need caution as a material.
TOP

MC703HL

Properties Test Methods Units Values
Density ASTM D-792
–
 1.11
Tensile Strength at 23°C ASTM D-638 MPa 66
{kgf/cm2} {670}
Tensile Elongation at 23°C
(at break)		 ASTM D-638 % 19
Tensile Modulus at 23°C ASTM D-638 MPa
–
{103kgf/cm2}
–
Compressive Strength at 23°C
(5% Deformation)		 ASTM D-695 MPa 75
{kgf/cm2} {760}
Compressive Modulus at 23°C ASTM D-695 MPa 2,765
{103kgf/cm2} {28.2}
Flexural Strength at 23°C ASTM D-790 MPa 92
{kgf/cm2} {940}
Flexural Modulus at 23°C ASTM D-790 MPa 2,599
{103kgf/cm2} {26.5}
Izod Impact (Notched) ASTM D-256 J/m 39
{kgf·cm/2.54cm} {10}
Rockwell Hardness at 23°C ASTM D-785 R scale 110
Heat Deflection Temperature ASTM D-648 °C 115
1.820MPa
{18.6kgf/cm2}
0.445MPa ASTM D-648 °C 215
{4.6kgf/cm2}
Coefficient of Liner Thermal Expansion ASTM D-696 ×10-5/°C 9.0
Continuous Service Temperature
–
 °C 110
Water Absorption Immersion at 23°C ASTM D-570 %  
(24h in water) 0.6
(Saturation) 8.0
Volume Resistivity at 23°C ASTM D-257 Ω·m
–
{Ω·cm}
–
Dielectric Strength ASTM D-149 kV/mm
–
Flammability UL94
–
 (HB)
* The data in the table shows the representive data, though they are not the guaranteed ones.
* Combustion property is presented according to UL standard evaluation test and data presented by raw material producers. No products need caution as a material.
TOP

MC602ST

Properties Test Methods Units Values
Density ASTM D-792
–
 1.23
Tensile Strength at 23°C ASTM D-638 MPa 96
{kgf/cm2} {979}
Tensile Elongation at 23°C
(at break)		 ASTM D-638 % 15
Tensile Modulus at 23°C ASTM D-638 MPa
–
{103kgf/cm2}
–
Compressive Strength at 23°C
(5% Deformation)		 ASTM D-695 MPa 115
{kgf/cm2} {1,173}
Compressive Modulus at 23°C ASTM D-695 MPa 4640
{103kgf/cm2} {47.3}
Flexural Strength at 23°C ASTM D-790 MPa 140
{kgf/cm2} {1,428}
Flexural Modulus at 23°C ASTM D-790 MPa 4,640
{103kgf/cm2} {47.3}
Izod Impact (Notched) ASTM D-256 J/m 45
{kgf·cm/2.54cm} {12}
Rockwell Hardness at 23°C ASTM D-785 R scale 120
Heat Deflection Temperature ASTM D-648 °C 200
1.820MPa
{18.6kgf/cm2}
0.445MPa ASTM D-648 °C
–
{4.6kgf/cm2}
Coefficient of Liner Thermal Expansion ASTM D-696 ×10-5/°C 6.5
Continuous Service Temperature
–
 °C 150
Water Absorption Immersion at 23°C ASTM D-570 %  
(24h in water) 0.5
(Saturation) 5.5
Volume Resistivity at 23°C ASTM D-257 Ω·m
–
{Ω·cm}
–
Dielectric Strength ASTM D-149 kV/mm
–
Flammability UL94
–
 (HB)
* The data in the table shows the representive data, though they are not the guaranteed ones.
* Combustion property is presented according to UL standard evaluation test and data presented by raw material producers. No products need caution as a material.
TOP

MC501CD R2

Properties Test Methods Units Values
Density ASTM D-792
–
 1.20
Tensile Strength at 23°C ASTM D-638 MPa 68
{kgf/cm2} {700}
Tensile Elongation at 23°C
(at break)		 ASTM D-638 % 10
Tensile Modulus at 23°C ASTM D-638 MPa
–
{103kgf/cm2}
–
Compressive Strength at 23°C
(5% Deformation)		 ASTM D-695 MPa 98
{kgf/cm2} {1,000}
Compressive Modulus at 23°C ASTM D-695 MPa 4,210
{103kgf/cm2} {43}
Flexural Strength at 23°C ASTM D-790 MPa 117
{kgf/cm2} {1,200}
Flexural Modulus at 23°C ASTM D-790 MPa 4,110
{103kgf/cm2} {42}
Izod Impact (Notched) ASTM D-256 J/m 35
{kgf·cm/2.54cm} {9}
Rockwell Hardness at 23°C ASTM D-785 R scale 119
Heat Deflection Temperature ASTM D-648 °C 200
1.820MPa
{18.6kgf/cm2}
0.445MPa ASTM D-648 °C 215
{4.6kgf/cm2}
Coefficient of Liner Thermal Expansion ASTM D-696 ×10-5/°C 8.0
Continuous Service Temperature
–
 °C 120
Water Absorption Immersion at 23°C ASTM D-570 %  
(24h in water) 0.4
(Saturation) 5.2
Volume Resistivity at 23°C ASTM D-257 Ω·m 1 - 102
{Ω·cm} {102 - 104}
Dielectric Strength ASTM D-149 kV/mm
–
Flammability UL94
–
 (HB)
* The data in the table shows the representive data, though they are not the guaranteed ones.
* Combustion property is presented according to UL standard evaluation test and data presented by raw material producers. No products need caution as a material.
TOP

MC501CD R6

Properties Test Methods Units Values
Density ASTM D-792
–
 1.23
Tensile Strength at 23°C ASTM D-638 MPa 74
{kgf/cm2} {760}
Tensile Elongation at 23°C
(at break)		 ASTM D-638 % 7
Tensile Modulus at 23°C ASTM D-638 MPa
–
{103kgf/cm2}
–
Compressive Strength at 23°C
(5% Deformation)		 ASTM D-695 MPa 93
{kgf/cm2} {950}
Compressive Modulus at 23°C ASTM D-695 MPa 4,020
{103kgf/cm2} {41}
Flexural Strength at 23°C ASTM D-790 MPa 117
{kgf/cm2} {1,200}
Flexural Modulus at 23°C ASTM D-790 MPa 4,020
{103kgf/cm2} {41}
Izod Impact (Notched) ASTM D-256 J/m 35
{kgf·cm/2.54cm} {9}
Rockwell Hardness at 23°C ASTM D-785 R scale 117
Heat Deflection Temperature ASTM D-648 °C 200
1.820MPa
{18.6kgf/cm2}
0.445MPa ASTM D-648 °C 215
{4.6kgf/cm2}
Coefficient of Liner Thermal Expansion ASTM D-696 ×10-5/°C 7.5
Continuous Service Temperature
–
 °C 120
Water Absorption Immersion at 23°C ASTM D-570 %  
(24h in water) 0.5
(Saturation) 5.7
Volume Resistivity at 23°C ASTM D-257 Ω·m 104 - 106
{Ω·cm} {106 - 108}
Dielectric Strength ASTM D-149 kV/mm
–
Flammability UL94
–
 (HB)
* The data in the table shows the representive data, though they are not the guaranteed ones.
* Combustion property is presented according to UL standard evaluation test and data presented by raw material producers. No products need caution as a material.
TOP

MC501CD R9

Properties Test Methods Units Values
Density ASTM D-792
–
 1.19
Tensile Strength at 23°C ASTM D-638 MPa 88
{kgf/cm2} {897}
Tensile Elongation at 23°C
(at break)		 ASTM D-638 % 12
Tensile Modulus at 23°C ASTM D-638 MPa
–
{103kgf/cm2}
–
Compressive Strength at 23°C
(5% Deformation)		 ASTM D-695 MPa 106
{kgf/cm2} {1,081}
Compressive Modulus at 23°C ASTM D-695 MPa 4,438
{103kgf/cm2} {45}
Flexural Strength at 23°C ASTM D-790 MPa 132
{kgf/cm2} {1,346}
Flexural Modulus at 23°C ASTM D-790 MPa 4,160
{103kgf/cm2} {42}
Izod Impact (Notched) ASTM D-256 J/m 35
{kgf·cm/2.54cm} {9}
Rockwell Hardness at 23°C ASTM D-785 R scale 119
Heat Deflection Temperature ASTM D-648 °C 200
1.820MPa
{18.6kgf/cm2}
0.445MPa ASTM D-648 °C 215
{4.6kgf/cm2}
Coefficient of Liner Thermal Expansion ASTM D-696 ×10-5/°C 8.6
Continuous Service Temperature
–
 °C 150
Water Absorption Immersion at 23°C ASTM D-570 %  
(24h in water) 0.6
(Saturation) 6.2
Volume Resistivity at 23°C ASTM D-257 Ω·m 106-108
{Ω·cm} {108-1010}
Dielectric Strength ASTM D-149 kV/mm
–
Flammability UL94
–
 (HB)
* The data in the table shows the representive data, though they are not the guaranteed ones.
* Combustion property is presented according to UL standard evaluation test and data presented by raw material producers. No products need caution as a material.
TOP

MC500AS R11

Properties Test Methods Units Values
Density ASTM D-792
–
 1.15
Tensile Strength at 23°C ASTM D-638 MPa 52
{kgf/cm2} {530}
Tensile Elongation at 23°C
(at break)		 ASTM D-638 % 162
Tensile Modulus at 23°C ASTM D-638 MPa
–
{103kgf/cm2}
–
Compressive Strength at 23°C
(5% Deformation)		 ASTM D-695 MPa 33
{kgf/cm2} {340}
Compressive Modulus at 23°C ASTM D-695 MPa 1,314
{103kgf/cm2} {13.4}
Flexural Strength at 23°C ASTM D-790 MPa 45
{kgf/cm2} {460}
Flexural Modulus at 23°C ASTM D-790 MPa 1,216
{103kgf/cm2} {12.4}
Izod Impact (Notched) ASTM D-256 J/m 180
{kgf·cm/2.54cm} {46.6}
Rockwell Hardness at 23°C ASTM D-785 R scale 93
Heat Deflection Temperature ASTM D-648 °C 75
1.820MPa
{18.6kgf/cm2}
0.445MPa ASTM D-648 °C 150
{4.6kgf/cm2}
Coefficient of Liner Thermal Expansion ASTM D-696 ×10-5/°C 11.0
Continuous Service Temperature
–
 °C 105
Water Absorption Immersion at 23°C ASTM D-570 %  
(24h in water) 1.6
(Saturation) 7.0
Volume Resistivity at 23°C ASTM D-257 Ω·m 108 - 1010
{Ω·cm} {1010 - 1012}
Dielectric Strength ASTM D-149 kV/mm
–
Flammability UL94
–
 (HB)
* The data in the table shows the representive data, though they are not the guaranteed ones.
* Combustion property is presented according to UL standard evaluation test and data presented by raw material producers. No products need caution as a material.
TOP