Co-polymer
| Properties |
Test Methods |
Units |
Values |
| Density |
ASTM D-792 |
– |
1.41 |
| Tensile Strength at 23°C |
ASTM D-638 |
MPa |
61 |
| {kgf/cm2} |
{620} |
Tensile Elongation at 23°C
(at break) |
ASTM D-638 |
% |
40 |
| Tensile Modulus at 23°C |
ASTM D-638 |
MPa |
2,824 |
| {103kgf/cm2} |
{28.8} |
Compressive Strength at 23°C
(10% Deformation) |
ASTM D-695 |
MPa |
103 |
| {kgf/cm2} |
{1,050} |
| Compressive Modulus at 23°C |
ASTM D-695 |
MPa |
2,700 |
| {103kgf/cm2} |
{27.5} |
| Flexural Strength at 23°C |
ASTM D-790 |
MPa |
89 |
| {kgf/cm2} |
{910} |
| Flexural Modulus at 23°C |
ASTM D-790 |
MPa |
2,589 |
| {103kgf/cm2} |
{26.4} |
| Izod Impact (Notched) |
ASTM D-256 |
J/m |
74 |
| {kgf·cm/2.54cm} |
{19.1} |
| Rockwell Hardness |
ASTM D-785 |
R scale |
119 |
| Heat Deflection Temperature |
ASTM D-648 |
°C |
110 |
| 1.820MPa |
| {18.6kgf/cm2} |
| 0.445MPa |
ASTM D-648 |
°C |
158 |
| {4.6kgf/cm2} |
| Coefficient of Liner Thermal Expansion |
ASTM D-696 |
×10-5/°C |
9.0 |
| Continuous Service Temperature |
– |
°C |
95 |
| Water Absorption Immersion |
ASTM D-570 |
% |
|
| (24h in water) |
0.22 |
| (Saturation) |
0.7 |
| Volume Resistivity |
ASTM D-257 |
Ω·m |
>1012 |
| {Ω·cm} |
{>1014} |
| Dielectric Strength |
ASTM D-149 |
kV/mm |
20 |
| Flammability |
UL94 |
– |
HB* |
| * |
The data in the table shows the representive data, though they are not the guaranteed ones. |
| * |
POM-NC is available. |
POM-Hyper
| Properties |
Test Methods |
Units |
Values |
| Density |
ASTM D-792 |
– |
1.41 |
| Tensile Strength at 23°C |
ASTM D-638 |
MPa |
61 |
| {kgf/cm2} |
{620} |
Tensile Elongation at 23°C
(at break) |
ASTM D-638 |
% |
40 |
| Tensile Modulus at 23°C |
ASTM D-638 |
MPa |
2,824 |
| {103kgf/cm2} |
{28.8} |
Compressive Strength at 23°C
(10% Deformation) |
ASTM D-695 |
MPa |
103 |
| {kgf/cm2} |
{1,050} |
| Compressive Modulus at 23°C |
ASTM D-695 |
MPa |
2,700 |
| {103kgf/cm2} |
{27.5} |
| Flexural Strength at 23°C |
ASTM D-790 |
MPa |
89 |
| {kgf/cm2} |
{910} |
| Flexural Modulus at 23°C |
ASTM D-790 |
MPa |
2,589 |
| {103kgf/cm2} |
{26.4} |
| Izod Impact (Notched) |
ASTM D-256 |
J/m |
74 |
| {kgf·cm/2.54cm} |
{19.1} |
| Rockwell Hardness |
ASTM D-785 |
R scale |
119 |
| Heat Deflection Temperature |
ASTM D-648 |
°C |
110 |
| 1.820MPa |
| {18.6kgf/cm2} |
| 0.445MPa |
ASTM D-648 |
°C |
158 |
| {4.6kgf/cm2} |
| Coefficient of Liner Thermal Expansion |
ASTM D-696 |
×10-5/°C |
9.0 |
| Continuous Service Temperature |
– |
°C |
95 |
| Water Absorption Immersion |
ASTM D-570 |
% |
|
| (24h in water) |
0.22 |
| (Saturation) |
0.7 |
| Volume Resistivity |
ASTM D-257 |
Ω·m |
>1012 |
| {Ω·cm} |
{>1014} |
| Dielectric Strength |
ASTM D-149 |
kV/mm |
20 |
| Flammability |
UL94 |
– |
HB* |
| * |
The data in the table shows the representive data, though they are not the guaranteed ones. |
| * |
POM-NC(HY) is available. |
Homo-polymer
| Properties |
Test Methods |
Units |
Values |
| Density |
ASTM D-792 |
– |
1.42 |
| Tensile Strength at 23°C |
ASTM D-638 |
MPa |
66 |
| {kgf/cm2} |
{670} |
Tensile Elongation at 23°C
(at break) |
ASTM D-638 |
% |
45 |
| Tensile Modulus at 23°C |
ASTM D-638 |
MPa |
2,910 |
| {103kgf/cm2} |
{29.7} |
Compressive Strength at 23°C
(10% Deformation) |
ASTM D-695 |
MPa |
113 |
| {kgf/cm2} |
{1,150} |
| Compressive Modulus at 23°C |
ASTM D-695 |
MPa |
2,900 |
| {103kgf/cm2} |
{29.6} |
| Flexural Strength at 23°C |
ASTM D-790 |
MPa |
94 |
| {kgf/cm2} |
{960} |
| Flexural Modulus at 23°C |
ASTM D-790 |
MPa |
2,790 |
| {103kgf/cm2} |
{28.5} |
| Izod Impact (Notched) |
ASTM D-256 |
J/m |
98 |
| {kgf·cm/2.54cm} |
{25} |
| Rockwell Hardness |
ASTM D-785 |
R scale |
120 |
| Heat Deflection Temperature |
ASTM D-648 |
°C |
120 |
| 1.820MPa |
| {18.6kgf/cm2} |
| 0.445MPa |
ASTM D-648 |
°C |
167 |
| {4.6kgf/cm2} |
| Coefficient of Liner Thermal Expansion |
ASTM D-696 |
×10-5/°C |
8.5 |
| Continuous Service Temperature |
– |
°C |
85 |
| Water Absorption Immersion |
ASTM D-570 |
% |
|
| (24h in water) |
0.22 |
| (Saturation) |
0.7 |
| Volume Resistivity |
ASTM D-257 |
Ω·m |
>1012 |
| {Ω·cm} |
{>1014} |
| Dielectric Strength |
ASTM D-149 |
kV/mm |
20 |
| Flammability |
UL94 |
– |
HB |
| * |
The data in the table shows the representive data, though they are not the guaranteed ones. |
POM-HL
| Properties |
Test Methods |
Units |
Values |
| Density |
ASTM D-792 |
– |
1.41 |
| Tensile Strength at 23°C |
ASTM D-638 |
MPa |
61 |
| {kgf/cm2} |
{620} |
Tensile Elongation at 23°C
(at break) |
ASTM D-638 |
% |
46 |
| Tensile Modulus at 23°C |
ASTM D-638 |
MPa |
– |
| {103kgf/cm2} |
– |
Compressive Strength at 23°C
(5% Deformation) |
ASTM D-695 |
MPa |
75 |
| {kgf/cm2} |
{765} |
| Compressive Modulus at 23°C |
ASTM D-695 |
MPa |
2,743 |
| {103kgf/cm2} |
{28.0} |
| Flexural Strength at 23°C |
ASTM D-790 |
MPa |
80.4 |
| {kgf/cm2} |
{820} |
| Flexural Modulus at 23°C |
ASTM D-790 |
MPa |
2,450 |
| {103kgf/cm2} |
{25.0} |
| Izod Impact (Notched) |
ASTM D-256 |
J/m |
59 |
| {kgf·cm/2.54cm} |
{15.2} |
| Rockwell Hardness |
ASTM D-785 |
R scale |
119 |
| Heat Deflection Temperature |
ASTM D-648 |
°C |
110 |
| 1.820MPa |
| {18.6kgf/cm2} |
| 0.445MPa |
ASTM D-648 |
°C |
– |
| {4.6kgf/cm2} |
| Coefficient of Liner Thermal Expansion |
ASTM D-696 |
×10-5/°C |
9.0 |
| Continuous Service Temperature |
– |
°C |
95 |
| Water Absorption Immersion |
ASTM D-570 |
% |
|
| (24h in water) |
– |
| (Saturation) |
– |
| Volume Resistivity |
ASTM D-257 |
Ω·m |
>1012 |
| {Ω·cm} |
{>1014} |
| Dielectric Strength |
ASTM D-149 |
kV/mm |
– |
| Flammability |
UL94 |
– |
(HB) |
| * |
The data in the table shows the representive data, though they are not the guaranteed ones. |
|