Ketron® 1000 PEEK Ketron® HPV PEEK Ketron® GF30 PEEK Ketron® CA30 PEEK

Ketron^® 1000 PEEK

Properties	Test Methods	Units	Values
Density	ASTM D-792	–	1.32
Tensile Strength at 23°C	ASTM D-638	MPa	98
		{kgf/cm2}	{1,000}
Tensile Elongation at 23°C (at break)	ASTM D-638	%	20
Tensile Modulus at 23°C	ASTM D-638	MPa	–
		{103kgf/cm2}	–
Compressive Strength at 23°C (5% Deformation)	ASTM D-695	MPa	119
		{kgf/cm2}	{1,210}
Compressive Modulus at 23°C	ASTM D-695	MPa	4,110
		{103kgf/cm2}	{42}
Flexural Strength at 23°C	ASTM D-790	MPa	170
		{kgf/cm2}	{1,730}
Flexural Modulus at 23°C	ASTM D-790	MPa	4,021
		{103kgf/cm2}	{41}
Izod Impact (Notched)	ASTM D-256	J/m	77
		{kgf·cm/2.54cm}	{20}
Rockwell Hardness at 23°C	ASTM D-785	R scale	120
Heat Deflection Temperature	ASTM D-648	°C	155
1.820MPa
{18.6kgf/cm2}
0.445MPa	ASTM D-648	°C	–
{4.6kgf/cm2}
Coefficient of Liner Thermal Expansion	ASTM D-696	×10-5/°C	5.0
Continuous Service Temperature	–	°C	250
Water Absorption Immersion at 23°C	ASTM D-570	%
(24h in water)			0.04
(Saturation)			0.5
Volume Resistivity at 23°C	ASTM D-257	Ω·m	1014
		{Ω·cm}	{1016}
Dielectric Strength	ASTM D-149	kV/mm	19
Flammability	UL94	–	V-0

Ketron^® HPV PEEK

Properties	Test Methods	Units	Values
Density	ASTM D-792	–	1.45
Tensile Strength at 23°C	ASTM D-638	MPa	75
		{kgf/cm2}	{765}
Tensile Elongation at 23°C (at break)	ASTM D-638	%	5
Tensile Modulus at 23°C	ASTM D-638	MPa	–
		{103kgf/cm2}	–
Compressive Strength at 23°C (5% Deformation)	ASTM D-695	MPa	107
		{kgf/cm2}	{1,090}
Compressive Modulus at 23°C	ASTM D-695	MPa	4,500
		{103kgf/cm2}	{46}
Flexural Strength at 23°C	ASTM D-790	MPa	97
		{kgf/cm2}	{990}
Flexural Modulus at 23°C	ASTM D-790	MPa	5,001
		{103kgf/cm2}	{51}
Izod Impact (Notched)	ASTM D-256	J/m	35
		{kgf·cm/2.54cm}	{9}
Rockwell Hardness at 23°C	ASTM D-785	R scale	120
Heat Deflection Temperature	ASTM D-648	°C	195
1.820MPa
{18.6kgf/cm2}
0.445MPa	ASTM D-648	°C	–
{4.6kgf/cm2}
Coefficient of Liner Thermal Expansion	ASTM D-696	×10-5/°C	5.0
Continuous Service Temperature	–	°C	250
Water Absorption Immersion at 23°C	ASTM D-570	%
(24h in water)			0.06
(Saturation)			–
Volume Resistivity at 23°C	ASTM D-257	Ω·m	–
		{Ω·cm}	–
Dielectric Strength	ASTM D-149	kV/mm	–
Flammability	UL94	–	V-0

Ketron^® GF30 PEEK

Properties	Test Methods	Units	Values
Density	ASTM D-792	–	1.51
Tensile Strength at 23°C	ASTM D-638	MPa	90
		{kgf/cm2}	{920}
Tensile Elongation at 23°C (at break)	ASTM D-638	%	5
Tensile Modulus at 23°C	ASTM D-638	MPa	–
		{103kgf/cm2}	–
Compressive Strength at 23°C (5% Deformation)	ASTM D-695	MPa	133
		{kgf/cm2}	{1,360}
Compressive Modulus at 23°C	ASTM D-695	MPa	6,060
		{103kgf/cm2}	{62}
Flexural Strength at 23°C	ASTM D-790	MPa	–
		{kgf/cm2}	–
Flexural Modulus at 23°C	ASTM D-790	MPa	–
		{103kgf/cm2}	–
Izod Impact (Notched)	ASTM D-256	J/m	55
		{kgf·cm/2.54cm}	{14}
Rockwell Hardness at 23°C	ASTM D-785	M scale	99
Heat Deflection Temperature	ASTM D-648	°C	230
1.820MPa
{18.6kgf/cm2}
0.445MPa	ASTM D-648	°C	–
{4.6kgf/cm2}
Coefficient of Liner Thermal Expansion	ASTM D-696	×10-5/°C	3.0
Continuous Service Temperature	–	°C	250
Water Absorption Immersion at 23°C	ASTM D-570	%
(24h in water)			–
(Saturation)			–
Volume Resistivity at 23°C	ASTM D-257	Ω·m	–
		{Ω·cm}	–
Dielectric Strength	ASTM D-149	kV/mm	–
Flammability	UL94	–	V-0

Ketron^® CA30 PEEK

Properties	Test Methods	Units	Values
Density	ASTM D-792	–	1.41
Tensile Strength at 23°C	ASTM D-638	MPa	130
		{kgf/cm2}	{1,330}
Tensile Elongation at 23°C (at break)	ASTM D-638	%	5
Tensile Modulus at 23°C	ASTM D-638	MPa	–
		{103kgf/cm2}	–
Compressive Strength at 23°C (5% Deformation)	ASTM D-695	MPa	144
		{kgf/cm2}	{1,470}
Compressive Modulus at 23°C	ASTM D-695	MPa	7,260
		{103kgf/cm2}	{74}
Flexural Strength at 23°C	ASTM D-790	MPa	227
		{kgf/cm2}	{2,320}
Flexural Modulus at 23°C	ASTM D-790	MPa	–
		{103kgf/cm2}	–
Izod Impact (Notched)	ASTM D-256	J/m	55
		{kgf·cm/2.54cm}	{14}
Rockwell Hardness at 23°C	ASTM D-785	M scale	102
Heat Deflection Temperature	ASTM D-648	°C	230
1.820MPa
{18.6kgf/cm2}
0.445MPa	ASTM D-648	°C	–
{4.6kgf/cm2}
Coefficient of Liner Thermal Expansion	ASTM D-696	×10-5/°C	2.5
Continuous Service Temperature	–	°C	250
Water Absorption Immersion at 23°C	ASTM D-570	%
(24h in water)			–
(Saturation)			–
Volume Resistivity at 23°C	ASTM D-257	Ω·m	103 - 104
		{Ω·cm}	{105 - 106}
Dielectric Strength	ASTM D-149	kV/mm	–
Flammability	UL94	–	V-0