[POLYPENCO® PET]
|
Ertalyte®
| Properties |
Test Methods |
Units |
Values |
| Density |
ASTM D-792 |
– |
1.39 |
| Tensile Strength at 23°C |
ASTM D-638 |
MPa |
84 |
| {kgf/cm2} |
{860} |
Tensile Elongation at 23°C
(at break) |
ASTM D-638 |
% |
20 |
| Tensile Modulus at 23°C |
ASTM D-638 |
MPa |
– |
| {103kgf/cm2} |
– |
Compressive Strength at 23°C
(5% Deformation) |
ASTM D-695 |
MPa |
97 |
| {kgf/cm2} |
{990} |
| Compressive Modulus at 23°C |
ASTM D-695 |
MPa |
3,293 |
| {103kgf/cm2} |
{33.6} |
| Flexural Strength at 23°C |
ASTM D-790 |
MPa |
127 |
| {kgf/cm2} |
{1,300} |
| Flexural Modulus at 23°C |
ASTM D-790 |
MPa |
3,011 |
| {103kgf/cm2} |
{30.7} |
| Izod Impact (Notched) |
ASTM D-256 |
J/m |
35 |
| {kgf·cm/2.54cm} |
{9.1} |
| Rockwell Hardness at 23°C |
ASTM D-785 |
R scale |
125 |
| Heat Deflection Temperature |
ASTM D-648 |
°C |
98 |
| 1.820MPa |
| {18.6kgf/cm2} |
| 0.445MPa |
ASTM D-648 |
°C |
194 |
| {4.6kgf/cm2} |
| Coefficient of Liner Thermal Expansion |
ASTM D-696 |
×10-5/°C |
6.0 |
| Continuous Service Temperature |
– |
°C |
100 |
| Water Absorption Immersion at 23°C |
ASTM D-570 |
% |
|
| (24h in water) |
0.07 |
| (Saturation) |
0.5 |
| Volume Resistivity at 23°C |
ASTM D-257 |
Ω·m |
>1014 |
| {Ω·cm} |
{>1016} |
| Dielectric Strength |
ASTM D-149 |
kV/mm |
22 |
| Flammability |
UL94 |
– |
(HB) |
| * |
The data in the table shows the representive data, though they are not the guaranteed ones. |
| * |
Combustion property is presented according to UL standard evaluation test and data presented by raw material producers. No products need caution as a material. |
Ertalyte® TX
| Properties |
Test Methods |
Units |
Values |
| Density |
ASTM D-792 |
– |
1.44 |
| Tensile Strength at 23°C |
ASTM D-638 |
MPa |
79 |
| {kgf/cm2} |
{810} |
Tensile Elongation at 23°C
(at break) |
ASTM D-638 |
% |
12 |
| Tensile Modulus at 23°C |
ASTM D-638 |
MPa |
– |
| {103kgf/cm2} |
– |
Compressive Strength at 23°C
(5% Deformation) |
ASTM D-695 |
MPa |
88 |
| {kgf/cm2} |
{900} |
| Compressive Modulus at 23°C |
ASTM D-695 |
MPa |
2,881 |
| {103kgf/cm2} |
{29.4} |
| Flexural Strength at 23°C |
ASTM D-790 |
MPa |
115 |
| {kgf/cm2} |
{1,170} |
| Flexural Modulus at 23°C |
ASTM D-790 |
MPa |
2,864 |
| {103kgf/cm2} |
{29.2} |
| Izod Impact (Notched) |
ASTM D-256 |
J/m |
40 |
| {kgf·cm/2.54cm} |
{10.4} |
| Rockwell Hardness at 23°C |
ASTM D-785 |
R scale |
102 |
| Heat Deflection Temperature |
ASTM D-648 |
°C |
114 |
| 1.820MPa |
| {18.6kgf/cm2} |
| 0.445MPa |
ASTM D-648 |
°C |
176 |
| {4.6kgf/cm2} |
| Coefficient of Liner Thermal Expansion |
ASTM D-696 |
×10-5/°C |
6.9 |
| Continuous Service Temperature |
– |
°C |
100 |
| Water Absorption Immersion at 23°C |
ASTM D-570 |
% |
|
| (24h in water) |
0.47 |
| (Saturation) |
– |
| Volume Resistivity at 23°C |
ASTM D-257 |
Ω·m |
>1014 |
| {Ω·cm} |
{>1016} |
| Dielectric Strength |
ASTM D-149 |
kV/mm |
21 |
| Flammability |
UL94 |
– |
(HB) |
| * |
The data in the table shows the representive data, though they are not the guaranteed ones. |
| * |
Combustion property is presented according to UL standard evaluation test and data presented by raw material producers. No products need caution as a material. |
|