[POLYPENCO® U-PE]
|
TIVAR® 1000·1000 HY
| Properties |
Test Methods |
Units |
Values |
| Density |
ASTM D-792 |
– |
0.94 |
| Tensile Strength at 23°C |
ASTM D-638 |
MPa |
31 |
| {kgf/cm2} |
{320} |
Tensile Elongation at 23°C
(at break) |
ASTM D-638 |
% |
500 |
| Tensile Modulus at 23°C |
ASTM D-638 |
MPa |
– |
| {103kgf/cm2} |
– |
Compressive Strength at 23°C
(5% Deformation) |
ASTM D-695 |
MPa |
20 |
| {kgf/cm2} |
{200} |
| Compressive Modulus at 23°C |
ASTM D-695 |
MPa |
774 |
| {103kgf/cm2} |
{7.9} |
| Flexural Strength at 23°C |
ASTM D-790 |
MPa |
20 |
| {kgf/cm2} |
{200} |
| Flexural Modulus at 23°C |
ASTM D-790 |
MPa |
883 |
| {103kgf/cm2} |
{9} |
| Izod Impact (Notched) |
ASTM D-256 |
J/m |
No break |
| {kgf·cm/2.54cm} |
| Rockwell Hardness at 23°C |
ASTM D-785 |
R scale |
52 |
| Heat Deflection Temperature |
ASTM D-648 |
°C |
54 |
| 1.820MPa |
| {18.6kgf/cm2} |
| 0.445MPa |
ASTM D-648 |
°C |
89 |
| {4.6kgf/cm2} |
| Coefficient of Liner Thermal Expansion |
ASTM D-696 |
×10-5/°C |
20.0 |
| Continuous Service Temperature |
– |
°C |
80 |
| Water Absorption Immersion at 23°C |
ASTM D-570 |
% |
|
| (24h in water) |
<0.01 |
| (Saturation) |
– |
| Volume Resistivity at 23°C |
ASTM D-257 |
Ω·m |
>1011 |
| {Ω·cm} |
{>1013} |
| Dielectric Strength |
ASTM D-149 |
kV/mm |
– |
| Flammability |
UL94 |
– |
(HB) |
| * |
The data in the table shows the representive data, though they are not the guaranteed ones. |
| * |
Combustion property is presented according to UL standard evaluation test and data presented by raw material producers. No products need caution as a material. |
TIVAR® 1000 ASTL
| Properties |
Test Methods |
Units |
Values |
| Density |
ASTM D-792 |
– |
0.95 |
| Tensile Strength at 23°C |
ASTM D-638 |
MPa |
35 |
| {kgf/cm2} |
{360} |
Tensile Elongation at 23°C
(at break) |
ASTM D-638 |
% |
300 |
| Tensile Modulus at 23°C |
ASTM D-638 |
MPa |
– |
| {103kgf/cm2} |
– |
Compressive Strength at 23°C
(5% Deformation) |
ASTM D-695 |
MPa |
25 |
| {kgf/cm2} |
{250} |
| Compressive Modulus at 23°C |
ASTM D-695 |
MPa |
970 |
| {103kgf/cm2} |
{9.9} |
| Flexural Strength at 23°C |
ASTM D-790 |
MPa |
25 |
| {kgf/cm2} |
{250} |
| Flexural Modulus at 23°C |
ASTM D-790 |
MPa |
1,103 |
| {103kgf/cm2} |
{11.3} |
| Izod Impact (Notched) |
ASTM D-256 |
J/m |
No break |
| {kgf·cm/2.54cm} |
| Rockwell Hardness at 23°C |
ASTM D-785 |
R scale |
52 |
| Heat Deflection Temperature |
ASTM D-648 |
°C |
55 |
| 1.820MPa |
| {18.6kgf/cm2} |
| 0.445MPa |
ASTM D-648 |
°C |
108 |
| {4.6kgf/cm2} |
| Coefficient of Liner Thermal Expansion |
ASTM D-696 |
×10-5/°C |
19.0 |
| Continuous Service Temperature |
– |
°C |
80 |
| Water Absorption Immersion at 23°C |
ASTM D-570 |
% |
|
| (24h in water) |
– |
| (Saturation) |
– |
| Volume Resistivity at 23°C |
ASTM D-257 |
Ω·m |
102 |
| {Ω·cm} |
{104} |
| Dielectric Strength |
ASTM D-149 |
kV/mm |
– |
| Flammability |
UL94 |
– |
(HB) |
| * |
The data in the table shows the representive data, though they are not the guaranteed ones. |
| * |
Combustion property is presented according to UL standard evaluation test and data presented by raw material producers. No products need caution as a material. |
|