Duratron® T4203 PAI Duratron® T4301 PAI Duratron® T5530 PAI

Duratron^® T4203 PAI

Properties	Test Methods	Units	Values
Density	ASTM D-792	–	1.40
Tensile Strength at 23°C	ASTM D-638	MPa	147
		{kgf/cm2}	{1,500}
Tensile Elongation at 23°C (at break)	ASTM D-638	%	35
Tensile Modulus at 23°C	ASTM D-638	MPa	–
		{103kgf/cm2}	–
Compressive Strength at 23°C (5% Deformation)	ASTM D-695	MPa	117
		{kgf/cm2}	{1,200}
Compressive Modulus at 23°C	ASTM D-695	MPa	3,820
		{103kgf/cm2}	{39}
Flexural Strength at 23°C	ASTM D-790	MPa	196
		{kgf/cm2}	{2,000}
Flexural Modulus at 23°C	ASTM D-790	MPa	3,620
		{103kgf/cm2}	{37}
Izod Impact (Notched)	ASTM D-256	J/m	138
		{kgf·cm/2.54cm}	{36}
Rockwell Hardness at 23°C	ASTM D-785	R scale	127
Heat Deflection Temperature	ASTM D-648	°C	278
1.820MPa
{18.6kgf/cm2}
0.445MPa	ASTM D-648	°C	–
{4.6kgf/cm2}
Coefficient of Liner Thermal Expansion	ASTM D-696	×10-5/°C	3.1
Continuous Service Temperature	–	°C	250
Water Absorption Immersion at 23°C	ASTM D-570	%
(24h in water)			0.33
(Saturation)			–
Volume Resistivity at 23°C	ASTM D-257	Ω·m	1015
		{Ω·cm}	{1017}
Dielectric Strength	ASTM D-149	kV/mm	23.6
Flammability	UL94	–	V-0

Duratron^® T4301 PAI

Properties	Test Methods	Units	Values
Density	ASTM D-792	–	1.45
Tensile Strength at 23°C	ASTM D-638	MPa	108
		{kgf/cm2}	{1,100}
Tensile Elongation at 23°C (at break)	ASTM D-638	%	8
Tensile Modulus at 23°C	ASTM D-638	MPa	–
		{103kgf/cm2}	–
Compressive Strength at 23°C (5% Deformation)	ASTM D-695	MPa	108
		{kgf/cm2}	{1,100}
Compressive Modulus at 23°C	ASTM D-695	MPa	4,700
		{103kgf/cm2}	{48}
Flexural Strength at 23°C	ASTM D-790	MPa	186
		{kgf/cm2}	{1,900}
Flexural Modulus at 23°C	ASTM D-790	MPa	5,000
		{103kgf/cm2}	{51}
Izod Impact (Notched)	ASTM D-256	J/m	77
		{kgf·cm/2.54cm}	{20}
Rockwell Hardness at 23°C	ASTM D-785	R scale	123
Heat Deflection Temperature	ASTM D-648	°C	278
1.820MPa
{18.6kgf/cm2}
0.445MPa	ASTM D-648	°C	–
{4.6kgf/cm2}
Coefficient of Liner Thermal Expansion	ASTM D-696	×10-5/°C	3.1
Continuous Service Temperature	–	°C	250
Water Absorption Immersion at 23°C	ASTM D-570	%
(24h in water)			0.28
(Saturation)			–
Volume Resistivity at 23°C	ASTM D-257	Ω·m	–
		{Ω·cm}	–
Dielectric Strength	ASTM D-149	kV/mm	23.6
Flammability	UL94	–	V-0

Duratron^® T5530 PAI

Properties	Test Methods	Units	Values
Density	ASTM D-792	–	1.55
Tensile Strength at 23°C	ASTM D-638	MPa	108
		{kgf/cm2}	{1,100}
Tensile Elongation at 23°C (at break)	ASTM D-638	%	5
Tensile Modulus at 23°C	ASTM D-638	MPa	3,792
		{103kgf/cm2}	{38.67}
Compressive Strength at 23°C (5% Deformation)	ASTM D-695	MPa	132
		{kgf/cm2}	{1,350}
Compressive Modulus at 23°C	ASTM D-695	MPa	5,000
		{103kgf/cm2}	{51}
Flexural Strength at 23°C	ASTM D-790	MPa	147
		{kgf/cm2}	{1,500}
Flexural Modulus at 23°C	ASTM D-790	MPa	5,490
		{103kgf/cm2}	{56}
Izod Impact (Notched)	ASTM D-256	J/m	54
		{kgf·cm/2.54cm}	{14}
Rockwell Hardness at 23°C	ASTM D-785	R scale	124
Heat Deflection Temperature	ASTM D-648	°C	271
1.820MPa
{18.6kgf/cm2}
0.445MPa	ASTM D-648	°C	–
{4.6kgf/cm2}
Coefficient of Liner Thermal Expansion	ASTM D-696	×10-5/°C	2.7
Continuous Service Temperature	–	°C	250
Water Absorption Immersion at 23°C	ASTM D-570	%
(24h in water)			0.3
(Saturation)			–
Volume Resistivity at 23°C	ASTM D-257	Ω·m	1014
		{Ω·cm}	{1016}
Dielectric Strength	ASTM D-149	kV/mm	27.6
Flammability	UL94	–	V-0